CuAl6Si2Fe ( CW301G )
| Gradd : | CuAl6Si2Fe |
| Rhif: | CW301G |
| Dosbarthiad: | Aloi copr-alwminiwm |
| Dwysedd | 7.7 g/cm % C2% B3 |
| Safon: | EN 12163: 1998 Copr ac aloion copr. Gwialen at ddibenion cyffredinol EN 12167: 1998 Copr ac aloion copr. Proffiliau a bar hirsgwar at ddibenion cyffredinol EN 12165: 1998 Copr ac aloion copr. Stoc gofannu gyr ac anwr EN 12420: 1999 Copr ac aloion copr. Forgings |
| Graddau cyfwerth: | Dim gwybodaeth |
Cyfansoddiad cemegol % o radd CuAl6Si2Fe ( CW301G )
| Ab | Os | Mn | Ni | Al | Pb | Zn | Sn | Eraill | - |
| 0.5 - 0.7 | 2 - 2.4 | uchafswm 0.1 | uchafswm 0.1 | 6 - 6.4 | uchafswm 0.05 | uchafswm 0.4 | uchafswm 0.1 | cyfanswm 0.2 | Cu - gweddill |
Priodweddau mecanyddol gradd CuAl6Si2Fe ( CW301G )
| Rm- Cryfder tynnol (MPa) (R500) | 500 |
| Rm- Cryfder tynnol (MPa) (R600) | 600 |
| Rp0.20.2% cryfder prawf (MPa) (R500) | 250 |
| Rp0.20.2% cryfder prawf (MPa) (R600) | 350 |
| A— Min. hiriad wrth dorri asgwrn (%) (R500) | 20 |
| A— Min. hiriad wrth dorri asgwrn (%) (R600) | 12 |
| Caledwch Brinell (HB): (H120)(R500) | 120 - 150 |
| Caledwch Brinell (HB): (H140)(R600) | 140 |
Proses castio
| GS | Castio tywod |
| GM | Castio llwydni parhaol |
| GZ | Castio allgyrchol |
| GC | Castio parhaus |
| Meddyg Teulu | Castio marw pwysau |
Amodau materol
| R | Cyflwr materol a ddynodwyd gan y gwerth lleiaf o gryfder tynnol gofyniad ar gyfer y cynnyrch gyda chryfder tynnol gorfodol a gofynion elongation |
| H | Cyflwr materol a ddynodwyd gan y gwerth lleiaf o ofyniad caledwch ar gyfer y cynnyrch gyda gofynion caledwch gorfodol |
Priodweddau mecanyddol
| REh | Cryfder cnwd lleiaf / Mindestwert der oberen Streckgrenze / Limite d elastigit minimale |
| Rm | Cryfder tynnol / Zugfestigkeit / Resistance a la traction |
| A | Lleiafswm elongation / Mindestwert der Bruchdehnung / Allongement minimal |
| J | Prawf effaith rhicyn / Kerbschlagbiegeversuch / Essai de flexion par choc |
|
CuAl6Si2Fe ( CW301G ) Aloi copr-alwminiwm |