CuPb1P ( CW113C )
| Gradd : | CuPb1P |
| Rhif: | CW113C |
| Dosbarthiad: | Aloi copr aloi isel |
| Dwysedd | 8.9 g/cm ³ |
| Safon: | EN 12164: 1998 Copr ac aloion copr. Gwialen at ddibenion peiriannu am ddim |
| Graddau cyfwerth: | Ewch yma |
Cyfansoddiad cemegol % o radd CuPb1P ( CW113C )
| P | Pb | Eraill | - |
| 0.003 - 0.012 | 0.7 - 1.5 | cyfanswm 0.1 | Cu - gweddill |
Priodweddau mecanyddol gradd CuPb1P ( CW113C )
| Rm- Cryfder tynnol (MPa) (R250) | 250 |
| Rm- Cryfder tynnol (MPa) (R300) | 300 |
| Rp0.20.2% cryfder prawf (MPa) (R250) | 200 |
| Rp0.20.2% cryfder prawf (MPa) (R300) | 250 |
| A— Min. hiriad wrth dorri asgwrn (%) (R250) | 7 |
| A— Min. hiriad wrth dorri asgwrn (%) (R300) | 5 |
| A— Min. elongation Lo=100mm (%) (R250) | 3 |
| A— Min. elongation Lo=100mm (%) (R300) | 2 |
| Caledwch Brinell (HB): (R250) | 90 |
| Caledwch Brinell (HB): (R300) | 100 |
Graddau cyfwerth â gradd CuPb1P ( CW113C )
Rhybudd! Dim ond ar gyfer cyfeirio
| UE EN |
Almaen DIN,WNr |
||
| CuPb1P |
|
Proses castio
| GS | Castio tywod |
| GM | Castio llwydni parhaol |
| GZ | Castio allgyrchol |
| GC | Castio parhaus |
| Meddyg Teulu | Castio marw pwysau |
Amodau materol
| R | Cyflwr materol a ddynodwyd gan y gwerth lleiaf o gryfder tynnol gofyniad ar gyfer y cynnyrch gyda chryfder tynnol gorfodol a gofynion elongation |
| H | Cyflwr materol a ddynodwyd gan y gwerth lleiaf o ofyniad caledwch ar gyfer y cynnyrch gyda gofynion caledwch gorfodol |
Priodweddau mecanyddol
| ReH | Cryfder cnwd lleiaf / Mindestwert der oberen Streckgrenze / Limite d elastigit minimale |
| Rm | Cryfder tynnol / Zugfestigkeit / Resistance a la traction |
| A | Lleiafswm elongation / Mindestwert der Bruchdehnung / Allongement minimal |
| J | Prawf effaith rhicyn / Kerbschlagbiegeversuch / Essai de flexion par choc |
|
CuPb1P ( CW113C ) Aloi copr ag aloi isel |