CuZr ( CW120C )
| Gradd : | CuZr |
| Rhif: | CW120C |
| Dosbarthiad: | Aloi copr aloi isel |
| Dwysedd | 8.9 g/cm ³ |
| Safon: | EN 12163: 1998 Copr ac aloion copr. Gwialen at ddibenion cyffredinol EN 12166: 1998 Copr ac aloion copr. Gwifren at ddibenion cyffredinol EN 12167: 1998 Copr ac aloion copr. Proffiliau a bar hirsgwar at ddibenion cyffredinol EN 12165: 1998 Copr ac aloion copr. Stoc gofannu gyr ac anwr EN 12420: 1999 Copr ac aloion copr. Forgings |
| Graddau cyfwerth: | Ewch yma |
Cyfansoddiad cemegol % o radd CuZr ( CW120C )
| Zr | Eraill | - |
| 0.1 - 0.2 | cyfanswm 0.1 | Cu - gweddill |
Priodweddau mecanyddol gradd CuZr ( CW120C )
| Rm- Cryfder tynnol (MPa) (R180) | 180 |
| Rm- Cryfder tynnol (MPa) (R300) | 300 |
| Rp0.20.2% cryfder prawf (MPa) (R180) | 40 |
| Rp0.20.2% cryfder prawf (MPa) (R300) | 200 |
| A— Min. hiriad wrth dorri asgwrn (%) (R180) | 30 |
| A— Min. hiriad wrth dorri asgwrn (%) (R300) | 20 |
| Caledwch Brinell (HB): (H040) | 40 - 60 |
| Caledwch Brinell (HB): (H090) | 90 - 130 |
Graddau cyfwerth â gradd CuZr ( CW120C )
Rhybudd! Dim ond ar gyfer cyfeirio
| UE EN |
Almaen DIN,WNr |
||
| CuZr |
|
Proses castio
| GS | Castio tywod |
| GM | Castio llwydni parhaol |
| GZ | Castio allgyrchol |
| GC | Castio parhaus |
| Meddyg Teulu | Castio marw pwysau |
Amodau materol
| R | Cyflwr materol a ddynodwyd gan y gwerth lleiaf o gryfder tynnol gofyniad ar gyfer y cynnyrch gyda chryfder tynnol gorfodol a gofynion elongation |
| H | Cyflwr materol a ddynodwyd gan y gwerth lleiaf o ofyniad caledwch ar gyfer y cynnyrch gyda gofynion caledwch gorfodol |
Priodweddau mecanyddol
| ReH | Cryfder cnwd lleiaf / Mindestwert der oberen Streckgrenze / Limite d elastigit minimale |
| Rm | Cryfder tynnol / Zugfestigkeit / Resistance a la traction |
| A | Lleiafswm elongation / Mindestwert der Bruchdehnung / Allongement minimal |
| J | Prawf effaith rhicyn / Kerbschlagbiegeversuch / Essai de flexion par choc |
|
CuZr ( CW120C ) Aloi copr ag aloi isel |