CuNi30Cr2FeMnSi-C ( CC382H )
| Gradd : | CuNi30Cr2FeMnSi-C |
| Rhif: | CC382H |
| Dosbarthiad: | Aloi copr-nicel |
| Safon: | EN 1982: 2008 Copr ac aloion copr. Ingotau a castiau |
| Graddau cyfwerth: | Dim gwybodaeth |
Cyfansoddiad cemegol % o radd CuNi30Cr2FeMnSi-C ( CC382H )
| Mae ôl-ddodiad -C yn cael ei ychwanegu at y dynodiad i nodi deunydd ar ffurf castiau |
| Ab | C | Os | Mn | Ni | P | S | Cr | Ti | Al | Zr | B | Pb | Se | Mg | Zn | Bi | Te | - |
| 0.5 - 1 | uchafswm 0.03 | 0.15 - 0.5 | 0.5 - 1 | 29 - 32 | uchafswm 0.01 | uchafswm 0.01 | 1.5 - 2 | uchafswm 0.25 | uchafswm 0.01 | uchafswm 0.15 | uchafswm 0.01 | uchafswm 0.005 | uchafswm 0.005 | uchafswm 0.01 | uchafswm 0.2 | uchafswm 0.002 | uchafswm 0.005 | Cu - gweddill |
Priodweddau mecanyddol gradd CuNi30Cr2FeMnSi-C ( CC382H )
| Rm- Cryfder tynnol (MPa) (GS) | 440 |
| Rp0.20.2% cryfder prawf (MPa) (GS) | 250 |
| A— Min. hiriad wrth dorri asgwrn (%) (GS) | 18 |
| Caledwch Brinell (HBW): (GS) | 115 |
Proses castio
| GS | Castio tywod |
| GM | Castio llwydni parhaol |
| GZ | Castio allgyrchol |
| GC | Castio parhaus |
| Meddyg Teulu | Castio marw pwysau |
Amodau materol
| R | Cyflwr materol a ddynodwyd gan y gwerth lleiaf o gryfder tynnol gofyniad ar gyfer y cynnyrch gyda chryfder tynnol gorfodol a gofynion elongation |
| H | Cyflwr materol a ddynodwyd gan y gwerth lleiaf o ofyniad caledwch ar gyfer y cynnyrch gyda gofynion caledwch gorfodol |
Priodweddau mecanyddol
| ReH | Cryfder cnwd lleiaf / Mindestwert der oberen Streckgrenze / Limite d elastigit minimale |
| Rm | Cryfder tynnol / Zugfestigkeit / Resistance a la traction |
| A | Lleiafswm elongation / Mindestwert der Bruchdehnung / Allongement minimal |
| J | Prawf effaith rhicyn / Kerbschlagbiegeversuch / Essai de flexion par choc |
|
CuNi30Cr2FeMnSi-C ( CC382H ) Aloi copr-nicel |