CuAl11Fe6Ni6-C ( CC334G )
| Gradd : | CuAl11Fe6Ni6-}C |
| Rhif: | CC334G |
| Dosbarthiad: | Aloi copr-alwminiwm |
| Safon: | EN 1982: 2008 Copr ac aloion copr. Ingotau a castiau |
| Graddau cyfwerth: | Ewch yma |
Cyfansoddiad cemegol % gradd CuAl11Fe6Ni6-C ( CC334G )
| Mae ôl-ddodiad -C yn cael ei ychwanegu at y dynodiad i nodi deunydd ar ffurf castiau |
| Fe | Os | Mn | Ni | Al | Cu | Pb | Mg | Zn | Sn |
| 4 - 7 | uchafswm 0.1 | uchafswm 2.5 | 4 - 7.5 | 10 - 12 | 72 - 82.5 | uchafswm 0.05 | uchafswm 0.05 | uchafswm 0.5 | uchafswm 0.2 |
Priodweddau mecanyddol gradd CuAl11Fe6Ni6-C ( CC334G )
| Rm- Cryfder tynnol (MPa) (GS) | 680 |
| Rm- Cryfder tynnol (MPa) (GM) neu (GZ) | 750 |
| Rp0.20.2% cryfder prawf (MPa) (GS) | 320 |
| Rp0.20.2% cryfder prawf (MPa) (GM) neu (GZ) | 380 |
| A— Min. hiriad wrth dorri asgwrn (%) (GS) neu (GZ) neu (GM) | 5 |
| Caledwch Brinell (HBW): (GS) | 170 |
| Caledwch Brinell (HBW): (GM) neu (GZ) | 185 |
Graddau cyfwerth â gradd CuAl11Fe6Ni6-C ( CC334G )
Rhybudd! Dim ond ar gyfer cyfeirio
| UE EN |
Almaen DIN,WNr |
||||||
| CuAl11Fe6Ni6-}C |
|
Proses castio
| GS | Castio tywod |
| GM | Castio llwydni parhaol |
| GZ | Castio allgyrchol |
| GC | Castio parhaus |
| Meddyg Teulu | Castio marw pwysau |
Amodau materol
| R | Cyflwr materol a ddynodwyd gan y gwerth lleiaf o gryfder tynnol gofyniad ar gyfer y cynnyrch gyda chryfder tynnol gorfodol a gofynion elongation |
| H | Cyflwr materol a ddynodwyd gan y gwerth lleiaf o ofyniad caledwch ar gyfer y cynnyrch gyda gofynion caledwch gorfodol |
Priodweddau mecanyddol
| REh | Cryfder cnwd lleiaf / Mindestwert der oberen Streckgrenze / Limite d elastigit minimale |
| Rm | Cryfder tynnol / Zugfestigkeit / Resistance a la traction |
| A | Lleiafswm elongation / Mindestwert der Bruchdehnung / Allongement minimal |
| J | Prawf effaith rhicyn / Kerbschlagbiegeversuch / Essai de flexion par choc |
|
CuAl11Fe6Ni6-C ( CC334G ) Aloi copr-alwminiwm |