CuZn39Pb1Al-B ( CB754S )
| Gradd : | CuZn39Pb1Al-B |
| Rhif: | CB754S |
| Dosbarthiad: | Aloi copr-sinc |
| Safon: | EN 1982: 2008 Copr ac aloion copr. Ingotau a castiau |
| Graddau cyfwerth: | Ewch yma |
Cyfansoddiad cemegol % o radd CuZn39Pb1Al-B ( CB754S )
| Ychwanegir ôl-ddodiad -B at y dynodiad i adnabod defnydd ar ffurf ingotau |
| Ab | Os | Mn | Ni | P | Al | Cu | Pb | Sn | - |
| uchafswm 0.7 | uchafswm 0.05 | uchafswm 0.5 | uchafswm 1 | uchafswm 0.02 | 0.1 - 0.8 | 58 - 62 | 0.5 - 2.4 | uchafswm 1 | Zn - gweddill; Cu yn cynnwys Ni |
Priodweddau mecanyddol gradd CuZn39Pb1Al-B ( CB754S )
| Rm- Cryfder tynnol (MPa) (GS) | 220 |
| Rm- Cryfder tynnol (MPa) (GM) neu (GZ) | 280 |
| Rp0.20.2% cryfder prawf (MPa) (GS) | 80 |
| Rp0.20.2% cryfder prawf (MPa) (GM) neu (GZ) | 120 |
| A— Min. hiriad wrth dorri asgwrn (%) (GS) | 15 |
| A— Min. hiriad wrth dorri asgwrn (%) (GM) neu (GZ) | 10 |
| Caledwch Brinell (HBW): (GS) | 65 |
| Caledwch Brinell (HBW): (GM) neu (GZ) | 70 |
Graddau cyfwerth â gradd CuZn39Pb1Al-B ( CB754S )
Rhybudd! Dim ond ar gyfer cyfeirio
| UE EN |
Almaen DIN,WNr |
||
| CuZn39Pb1Al-B |
|
Proses castio
| GS | Castio tywod |
| GM | Castio llwydni parhaol |
| GZ | Castio allgyrchol |
| GC | Castio parhaus |
| Meddyg Teulu | Castio marw pwysau |
Amodau materol
| R | Cyflwr materol a ddynodwyd gan y gwerth lleiaf o gryfder tynnol gofyniad ar gyfer y cynnyrch gyda chryfder tynnol gorfodol a gofynion elongation |
| H | Cyflwr materol a ddynodwyd gan y gwerth lleiaf o ofyniad caledwch ar gyfer y cynnyrch gyda gofynion caledwch gorfodol |
Priodweddau mecanyddol
| REh | Cryfder cnwd lleiaf / Mindestwert der oberen Streckgrenze / Limite d elastigit minimale |
| Rm | Cryfder tynnol / Zugfestigkeit / Resistance a la traction |
| A | Lleiafswm elongation / Mindestwert der Bruchdehnung / Allongement minimal |
| J | Prawf effaith rhicyn / Kerbschlagbiegeversuch / Essai de flexion par choc |
|
CuZn39Pb1Al-B ( CB754S ) Aloi copr-sinc |