CuZn38AlFeNiPbSn ( CW715R )
| Gradd : | CuZn38AlFeNiPbSn |
| Rhif: | CW715R |
| Dosbarthiad: | Aloi cwpanaid |
| Dwysedd | 8.3 g% 2fcm % C2% B3 |
| Safon: | EN 1653: 1998 Copr ac aloion copr. Plât, dalen a chylchoedd ar gyfer boeleri, llestri gwasgedd ac unedau storio dŵr poeth |
| Graddau cyfwerth: | Dim gwybodaeth |
Cyfansoddiad cemegol % o radd CuZn38AlFeNiPbSn ( CW715R )
| Ab | Ni | Al | Cu | Fel | Pb | Sn | Eraill | - |
| 0.1 - 0.4 | 0.2 - 0.5 | 0.1 - 0.5 | 59 - 60.7 | uchafswm 0.05 | 0.3 - 0.7 | 0.3 - 0.6 | cyfanswm 0.2 | Zn — gweddill |
Priodweddau mecanyddol o radd CuZn38AlFeNiPbSn ( CW715R )
| Rm- Cryfder tynnol (MPa) (R390) | 390 |
| Rm- Cryfder tynnol (MPa) (R430) | 430 |
| Rp0.20.2% cryfder prawf (MPa) (R390) | 140 |
| Rp0.20.2% cryfder prawf (MPa) (R430) | 200 |
| A— Min. hiriad wrth dorri asgwrn (%) (R390) | 25 |
| A— Min. hiriad wrth dorri asgwrn (%) (R430) | 20 |
| caledwch Vickers (HV): (R390) | 110 |
| caledwch Vickers (HV): (R430) | 120 |
Proses castio
| GS | Castio tywod |
| GM | Castio llwydni parhaol |
| GZ | Castio allgyrchol |
| GC | Castio parhaus |
| Meddyg Teulu | Castio marw pwysau |
Amodau materol
| R | Cyflwr materol a ddynodwyd gan y gwerth lleiaf o gryfder tynnol gofyniad ar gyfer y cynnyrch gyda chryfder tynnol gorfodol a gofynion elongation |
| H | Cyflwr materol a ddynodwyd gan y gwerth lleiaf o ofyniad caledwch ar gyfer y cynnyrch gyda gofynion caledwch gorfodol |
Priodweddau mecanyddol
| REh | Cryfder cnwd lleiaf / Mindestwert der oberen Streckgrenze / Limite d elastigit minimale |
| Rm | Cryfder tynnol / Zugfestigkeit / Resistance a la traction |
| A | Lleiafswm elongation / Mindestwert der Bruchdehnung / Allongement minimal |
| J | Prawf effaith rhicyn / Kerbschlagbiegeversuch / Essai de flexion par choc |
|
CuZn38AlFeNiPbSn ( CW715R ) Aloi cwpan |