| Gradd : | CuZn31Si1 |
| Rhif: | CW708R |
| Dosbarthiad: | Aloi copr-sinc cymhleth |
| Dwysedd | 8.4 g/cm ³ |
| Safon: | EN 12163: 1998 Copr ac aloion copr. Gwialen at ddibenion cyffredinol EN 12449: 1999 Copr ac aloion copr. Tiwbiau crwn, di-dor at ddibenion cyffredinol |
| Graddau cyfwerth: | Ewch yma |
Cyfansoddiad cemegol % o radd CuZn31Si1 ( CW708R )
| Fe | Si | Ni | Cu | Pb | Eraill | - |
| uchafswm 0.4 | 0.7 - 1.3 | uchafswm 0.5 | 66 - 70 | uchafswm 0.8 | cyfanswm 0.5 | Zn — gweddill |
Priodweddau mecanyddol o radd CuZn31Si1 ( CW708R )
| Rm- Cryfder tynnol (MPa) (R460) | 460 |
| Rm- Cryfder tynnol (MPa) (R530) | 530 |
| Rp0.20.2% cryfder prawf (MPa) (R460) | 250 |
| Rp0.20.2% cryfder prawf (MPa) (R530) | 330 |
| A— Min. hiriad wrth dorri asgwrn (%) (R460) | 22 |
| A— Min. hiriad wrth dorri asgwrn (%) (R530) | 12 |
| Caledwch Brinell (HB): (H115) | 115 - 145 |
| Caledwch Brinell (HB): (H140) | 140 |
Graddau cyfwerth â gradd CuZn31Si1 ( CW708R )
Rhybudd! Dim ond ar gyfer cyfeirio
| UE EN |
Almaen DIN,WNr |
||
| CuZn31Si1 |
|
Proses castio
| GS | Castio tywod |
| GM | Castio llwydni parhaol |
| GZ | Castio allgyrchol |
| GC | Castio parhaus |
| Meddyg Teulu | Castio marw pwysau |
Amodau materol
| R | Cyflwr materol a ddynodwyd gan y gwerth lleiaf o gryfder tynnol gofyniad ar gyfer y cynnyrch gyda chryfder tynnol gorfodol a gofynion elongation |
| H | Cyflwr materol a ddynodwyd gan y gwerth lleiaf o ofyniad caledwch ar gyfer y cynnyrch gyda gofynion caledwch gorfodol |
Priodweddau mecanyddol
| ReH | Cryfder cnwd lleiaf / Mindestwert der oberen Streckgrenze / Limite d elastigit minimale |
| Rm | Cryfder tynnol / Zugfestigkeit / Resistance a la traction |
| A | Lleiafswm elongation / Mindestwert der Bruchdehnung / Allongement minimal |
| J | Prawf effaith rhicyn / Kerbschlagbiegeversuch / Essai de flexion par choc |
|
CuZn31Si1 ( CW708R ) Aloi copr-sinc cymhleth |