CuZn28Sn1As ( CW706R )
| Gradd : | CuZn28Sn1As |
| Rhif: | CW706R |
| Dosbarthiad: | Aloi cwpanaid |
| Dwysedd | 8.5 g% 2fcm % C2% B3 |
| Safon: | EN 12451: 1999 Copr ac aloion copr. Tiwbiau crwn, di-dor ar gyfer cyfnewidwyr gwres EN 12452: 1999 Copr ac aloion copr. Tiwbiau di-dor wedi'u rholio, finned, ar gyfer cyfnewidwyr gwres |
| Graddau cyfwerth: | Dim gwybodaeth |
Cyfansoddiad cemegol % o radd CuZn28Sn1As ( CW706R )
| Ab | Mn | Ni | P | Cu | Fel | Pb | Sn | Eraill | - |
| uchafswm 0.07 | uchafswm 0.1 | uchafswm 0.1 | uchafswm 0.01 | 70 - 72.5 | 0.02 - 0.06 | uchafswm 0.05 | 0.9 - 1.3 | cyfanswm 0.3 | Zn — gweddill |
Priodweddau mecanyddol gradd CuZn28Sn1As ( CW706R )
| Rm- Cryfder tynnol (MPa) (R320) | 320 |
| Rm- Cryfder tynnol (MPa) (R360) | 360 |
| Rp0.20.2% cryfder prawf (MPa) (R320) | 100 |
| Rp0.20.2% cryfder prawf (MPa) (R360) | 140 |
| A— Min. hiriad wrth dorri asgwrn (%) (R320) | 55 |
| A— Min. hiriad wrth dorri asgwrn (%) (R360) | 45 |
| caledwch Vickers (HV): (H060) (R320) | 60 - 90 |
| Caledwch Vickers (HV): (H080) (R360) | 80 - 110 |
Proses castio
| GS | Castio tywod |
| GM | Castio llwydni parhaol |
| GZ | Castio allgyrchol |
| GC | Castio parhaus |
| Meddyg Teulu | Castio marw pwysau |
Amodau materol
| R | Cyflwr materol a ddynodwyd gan y gwerth lleiaf o gryfder tynnol gofyniad ar gyfer y cynnyrch gyda chryfder tynnol gorfodol a gofynion elongation |
| H | Cyflwr materol a ddynodwyd gan y gwerth lleiaf o ofyniad caledwch ar gyfer y cynnyrch gyda gofynion caledwch gorfodol |
Priodweddau mecanyddol
| ReH | Cryfder cnwd lleiaf / Mindestwert der oberen Streckgrenze / Limite d elastigit minimale |
| Rm | Cryfder tynnol / Zugfestigkeit / Resistance a la traction |
| A | Lleiafswm elongation / Mindestwert der Bruchdehnung / Allongement minimal |
| J | Prawf effaith rhicyn / Kerbschlagbiegeversuch / Essai de flexion par choc |
|
CuZn28Sn1As ( CW706R ) Aloi cwpan |