CuZn23Al3Co ( CW703R )
| Gradd : | CuZn23Al3Co |
| Rhif: | CW703R |
| Dosbarthiad: | Aloi cwpanaid |
| Dwysedd | 8.2 g/cm ³ |
| Safon: | EN 1654: 1998 Copr ac aloion copr. Stribed ar gyfer ffynhonnau a chysylltwyr |
| Graddau cyfwerth: | Dim gwybodaeth |
Cyfansoddiad cemegol % o radd CuZn23Al3Co ( CW703R )
| Fe | Ni | Co | Al | Cu | Pb | Sn | Eraill | - |
| uchafswm 0.05 | uchafswm 0.3 | 0.25 - 0.55 | 3 - 3.8 | 72 - 75 | uchafswm 0.05 | uchafswm 0.1 | cyfanswm 0.1 | Zn — gweddill |
Priodweddau mecanyddol gradd CuZn23Al3Co ( CW703R )
| Rm- Cryfder tynnol (MPa) (R660) | 660-750 |
| Rm- Cryfder tynnol (MPa) (R740) | 740-830 |
| Rp0.20.2% cryfder prawf (MPa) (R660) | 580 |
| Rp0.20.2% cryfder prawf (MPa) (R740) | 660 |
| A— Min. elongation Lo=50mm (%) (R660) | 8-10 |
| A— Min. elongation Lo=50mm (%) (R740) | 3 |
| Caledwch Vickers (HV): (H190) (R660) | 190 - 220 |
| caledwch Vickers (HV): (H210) (R740) | 210 - 240 |
Priodweddau CuZn23Al3Co
| Modwlws elastigedd=115 kN/mm ² Dargludedd trydanol=10 MS/m; |
Proses castio
| GS | Castio tywod |
| GM | Castio llwydni parhaol |
| GZ | Castio allgyrchol |
| GC | Castio parhaus |
| Meddyg Teulu | Castio marw pwysau |
Amodau materol
| R | Cyflwr materol a ddynodwyd gan y gwerth lleiaf o gryfder tynnol gofyniad ar gyfer y cynnyrch gyda chryfder tynnol gorfodol a gofynion elongation |
| H | Cyflwr materol a ddynodwyd gan y gwerth lleiaf o ofyniad caledwch ar gyfer y cynnyrch gyda gofynion caledwch gorfodol |
Priodweddau mecanyddol
| ReH | Cryfder cnwd lleiaf / Mindestwert der oberen Streckgrenze / Limite d elastigit minimale |
| Rm | Cryfder tynnol / Zugfestigkeit / Resistance a la traction |
| A | Lleiafswm elongation / Mindestwert der Bruchdehnung / Allongement minimal |
| J | Prawf effaith rhicyn / Kerbschlagbiegeversuch / Essai de flexion par choc |
|
CuZn23Al3Co ( CW703R ) Aloi cwpan |