CuSn8PbP ( CW460K )
| Gradd : | CuSn8PbP |
| Rhif: | CW460K |
| Dosbarthiad: | Aloi copr-tun |
| Dwysedd | 8.8 g/cm % C2% B3 |
| Safon: | EN 12449: 1999 Copr ac aloion copr. Tiwbiau crwn, di-dor at ddibenion cyffredinol |
| Graddau cyfwerth: | Dim gwybodaeth |
Cyfansoddiad cemegol % o radd CuSn8PbP ( CW460K )
| Ab | Ni | P | Pb | Zn | Sn | Eraill | - |
| uchafswm 0.1 | uchafswm 0.3 | 0.2 - 0.4 | 0.1 - 0.5 | uchafswm 0.3 | 7.5 - 9 | cyfanswm 0.2 | Cu - gweddill |
Priodweddau mecanyddol gradd CuSn8PbP ( CW460K )
| Rm- Cryfder tynnol (MPa) (R460) | 460 |
| Rm- Cryfder tynnol (MPa) (R550) | 550 |
| Rm- Cryfder tynnol (MPa) (R620) | 620 |
| Rp0.20.2% cryfder prawf (MPa) (R460) | 280 |
| Rp0.20.2% cryfder prawf (MPa) (R550) | 480 |
| Rp0.20.2% cryfder prawf (MPa) (R620) | 540 |
| A— Min. hiriad wrth dorri asgwrn (%) (R460) | 30 |
| A— Min. hiriad wrth dorri asgwrn (%) (R550) | 12 |
| A— Min. hiriad wrth dorri asgwrn (%) (R620) | 5 |
| Caledwch Vickers (HV): (H130) (R460) | 130 - 165 |
| caledwch Vickers (HV): (H165) (R550) | 165 - 195 |
| caledwch Vickers (HV): (H180) (R620) | 180 |
Proses castio
| GS | Castio tywod |
| GM | Castio llwydni parhaol |
| GZ | Castio allgyrchol |
| GC | Castio parhaus |
| Meddyg Teulu | Castio marw pwysau |
Amodau materol
| R | Cyflwr materol a ddynodwyd gan y gwerth lleiaf o gryfder tynnol gofyniad ar gyfer y cynnyrch gyda chryfder tynnol gorfodol a gofynion elongation |
| H | Cyflwr materol a ddynodwyd gan y gwerth lleiaf o ofyniad caledwch ar gyfer y cynnyrch gyda gofynion caledwch gorfodol |
Priodweddau mecanyddol
| REh | Cryfder cnwd lleiaf / Mindestwert der oberen Streckgrenze / Limite d elastigit minimale |
| Rm | Cryfder tynnol / Zugfestigkeit / Resistance a la traction |
| A | Lleiafswm elongation / Mindestwert der Bruchdehnung / Allongement minimal |
| J | Prawf effaith rhicyn / Kerbschlagbiegeversuch / Essai de flexion par choc |
|
CuSn8PbP ( CW460K ) Aloi tun copr |