CuSn11Pb2-C ( CC482K )
| Gradd : | CuSn11Pb2-C |
| Rhif: | CC482K |
| Dosbarthiad: | Aloi copr-tun |
| Safon: | EN 1982: 2008 Copr ac aloion copr. Ingotau a castiau |
| Graddau cyfwerth: | Ewch yma |
Cyfansoddiad cemegol % o radd CuSn11Pb2-C ( CC482K )
| Mae ôl-ddodiad -C yn cael ei ychwanegu at y dynodiad i nodi deunydd ar ffurf castiau |
| Fe | Si | Mn | Ni | P | S | Al | Cu | Pb | Zn | Mae sb | Sn |
| uchafswm 0.2 | uchafswm 0.01 | uchafswm 0.2 | uchafswm 2 | uchafswm 0.4 | uchafswm 0.08 | uchafswm 0.01 | 83.5 - 87 | 0.7 - 2.5 | uchafswm 2 | uchafswm 0.2 | 10.5 - 12.5 |
Priodweddau mecanyddol gradd CuSn11Pb2-C ( CC482K )
| Rm- Cryfder tynnol (MPa) (GS) | 240 |
| Rm- Cryfder tynnol (MPa) (GZ) neu (GC) | 280 |
| Rp0.20.2% cryfder prawf (MPa) (GS) | 130 |
| Rp0.20.2% cryfder prawf (MPa) (GZ) neu (GC) | 150 |
| A— Min. hiriad wrth dorri asgwrn (%) (GS) neu (GZ) neu (GC) | 5 |
| Caledwch Brinell (HBW): (GS) | 80 |
| Caledwch Brinell (HBW): (GZ) neu (GC) | 90 |
Graddau cyfwerth â gradd CuSn11Pb2-C ( CC482K )
Rhybudd! Dim ond ar gyfer cyfeirio
| UE EN |
Almaen DIN,WNr |
||||||
| CuSn11Pb2-C |
|
Proses castio
| GS | Castio tywod |
| GM | Castio llwydni parhaol |
| GZ | Castio allgyrchol |
| GC | Castio parhaus |
| Meddyg Teulu | Castio marw pwysau |
Amodau materol
| R | Cyflwr materol a ddynodwyd gan y gwerth lleiaf o gryfder tynnol gofyniad ar gyfer y cynnyrch gyda chryfder tynnol gorfodol a gofynion elongation |
| H | Cyflwr materol a ddynodwyd gan y gwerth lleiaf o ofyniad caledwch ar gyfer y cynnyrch gyda gofynion caledwch gorfodol |
Priodweddau mecanyddol
| ReH | Cryfder cnwd lleiaf / Mindestwert der oberen Streckgrenze / Limite d elastigit minimale |
| Rm | Cryfder tynnol / Zugfestigkeit / Resistance a la traction |
| A | Lleiafswm elongation / Mindestwert der Bruchdehnung / Allongement minimal |
| J | Prawf effaith rhicyn / Kerbschlagbiegeversuch / Essai de flexion par choc |
|
CuSn11Pb2-C ( CC482K ) Aloi tun copr |