CuSn0.15 ( CW117C )
| Gradd : | CuSn0.15 |
| Rhif: | CW117C |
| Dosbarthiad: | Aloi copr aloi isel |
| Dwysedd | 8.9 g% 2fcm % C2% B3 |
| Safon: | EN 1758: 1998 Copr ac aloion copr. Stribed ar gyfer fframiau plwm EN 13148: 2001 Copr ac aloion copr. Stribed tun dip poeth |
| Graddau cyfwerth: | Dim gwybodaeth |
Cyfansoddiad cemegol % o radd CuSn0.15 ( CW117C )
| Ab | Ni | P | Zn | Sn | Eraill | - |
| uchafswm 0.02 | uchafswm 0.02 | uchafswm 0.015 | uchafswm 0.1 | 0.1 - 0.15 | cyfanswm 0.1 | Cu - gweddill |
Priodweddau mecanyddol gradd CuSn0.15 ( CW117C )
| Rm- Cryfder tynnol (MPa) (R300) | 300-370 |
| Rm- Cryfder tynnol (MPa) (R360) | 360-430 |
| Rm- Cryfder tynnol (MPa) (R420) | 420-490 |
| A— Min. elongation Lo=50mm (%) (R300) | 4 |
| A— Min. elongation Lo=50mm (%) (R360) | 3 |
| A— Min. elongation Lo=50mm (%) (R420) | 2 |
| caledwch Vickers (HV): (H085) | 85 - 110 |
| caledwch Vickers (HV): (H105) | 105 - 130 |
| caledwch Vickers (HV): (H120) | 120 - 140 |
Priodweddau CuSn0.15
| Cyfernod llinol ehangiad termol=17.3*10(-6) 1/K; Dargludedd trydanol=47 MS/m; |
Proses castio
| GS | Castio tywod |
| GM | Castio llwydni parhaol |
| GZ | Castio allgyrchol |
| GC | Castio parhaus |
| Meddyg Teulu | Castio marw pwysau |
Amodau materol
| R | Cyflwr materol a ddynodwyd gan y gwerth lleiaf o gryfder tynnol gofyniad ar gyfer y cynnyrch gyda chryfder tynnol gorfodol a gofynion elongation |
| H | Cyflwr materol a ddynodwyd gan y gwerth lleiaf o ofyniad caledwch ar gyfer y cynnyrch gyda gofynion caledwch gorfodol |
Priodweddau mecanyddol
| REh | Cryfder cnwd lleiaf / Mindestwert der oberen Streckgrenze / Limite d elastigit minimale |
| Rm | Cryfder tynnol / Zugfestigkeit / Resistance a la traction |
| A | Lleiafswm elongation / Mindestwert der Bruchdehnung / Allongement minimal |
| J | Prawf effaith rhicyn / Kerbschlagbiegeversuch / Essai de flexion par choc |
|
CuSn0.15 ( CW117C ) Aloi copr ag aloi isel |