CuNi7Zn39Pb3Mn2 ( CW400J )
| Gradd : | CuNi7Zn39Pb3Mn2 |
| Rhif: | CW400J |
| Dosbarthiad: | Aloi copr-nicel-sinc |
| Dwysedd | 8.5 g/cm ³ |
| Safon: | EN 12164: 1998 Copr ac aloion copr. Gwialen at ddibenion peiriannu am ddim EN 12166: 1998 Copr ac aloion copr. Gwifren at ddibenion cyffredinol EN 12167: 1998 Copr ac aloion copr. Proffiliau a bar hirsgwar at ddibenion cyffredinol EN 12165: 1998 Copr ac aloion copr. Stoc gofannu gyr ac anwr EN 12420: 1999 Copr ac aloion copr. Forgings |
| Graddau cyfwerth: | Dim gwybodaeth |
Cyfansoddiad cemegol % o radd CuNi7Zn39Pb3Mn2 ( CW400J )
| Fe | Mn | Ni | Cu | Pb | Sn | Eraill | - |
| uchafswm 0.3 | 1.5 - 3 | 6 - 8 | 47 - 50 | 2.3 - 3.3 | uchafswm 0.2 | cyfanswm 0.2 | Zn — gweddill |
Priodweddau mecanyddol gradd CuNi7Zn39Pb3Mn2 ( CW400J )
| Rm- Cryfder tynnol (MPa) (R510) | 510 |
| Rp0.20.2% cryfder prawf (MPa) (R510) | 400 |
| A— Min. hiriad wrth dorri asgwrn (%) (R510) | 12 |
| A— Min. elongation Lo=100mm (%) (R510) | 8 |
| Caledwch Brinell (HB): (R510) | 150 |
Proses castio
| GS | Castio tywod |
| GM | Castio llwydni parhaol |
| GZ | Castio allgyrchol |
| GC | Castio parhaus |
| Meddyg Teulu | Castio marw pwysau |
Amodau materol
| R | Cyflwr materol a ddynodwyd gan y gwerth lleiaf o gryfder tynnol gofyniad ar gyfer y cynnyrch gyda chryfder tynnol gorfodol a gofynion elongation |
| H | Cyflwr materol a ddynodwyd gan y gwerth lleiaf o ofyniad caledwch ar gyfer y cynnyrch gyda gofynion caledwch gorfodol |
Priodweddau mecanyddol
| ReH | Cryfder cnwd lleiaf / Mindestwert der oberen Streckgrenze / Limite d elastigit minimale |
| Rm | Cryfder tynnol / Zugfestigkeit / Resistance a la traction |
| A | Lleiafswm elongation / Mindestwert der Bruchdehnung / Allongement minimal |
| J | Prawf effaith rhicyn / Kerbschlagbiegeversuch / Essai de flexion par choc |
|
CuNi7Zn39Pb3Mn2 ( CW400J ) Aloi copr-nicel-sinc |