CuNi1P ( CW108C )
| Gradd : | CuNi1P |
| Rhif: | CW108C |
| Dosbarthiad: | Aloi copr aloi isel |
| Safon: | EN 12163: 1998 Copr ac aloion copr. Gwialen at ddibenion cyffredinol |
| Graddau cyfwerth: | Dim gwybodaeth |
Cyfansoddiad cemegol % o radd CuNi1P ( CW108C )
| Ni | P | Eraill | - |
| 0.8 - 1.2 | 0.15 - 0.25 | cyfanswm 0.1 | Cu - gweddill |
Priodweddau mecanyddol gradd CuNi1P ( CW108C )
| Rm- Cryfder tynnol (MPa) (R250) | 250 |
| Rm- Cryfder tynnol (MPa) (R400) | 400 |
| Rm- Cryfder tynnol (MPa) (R650) | 650 |
| Rm- Cryfder tynnol (MPa) (R700) | 700 |
| Rp0.20.2% cryfder prawf (MPa) (R250) | 140 |
| Rp0.20.2% cryfder prawf (MPa) (R400) | 330 |
| Rp0.20.2% cryfder prawf (MPa) (R650) | 500 |
| Rp0.20.2% cryfder prawf (MPa) (R700) | 630 |
| A— Min. hiriad wrth dorri asgwrn (%) (R250) | 25 |
| A— Min. hiriad wrth dorri asgwrn (%) (R400) | 10 |
| A— Min. hiriad wrth dorri asgwrn (%) (R700) | 7 |
| caledwch Vickers (HV): (H065) | 70 - 100 |
| caledwch Vickers (HV): (H110) | 115 - 165 |
| caledwch Vickers (HV): (H200) | 210 |
Proses castio
| GS | Castio tywod |
| GM | Castio llwydni parhaol |
| GZ | Castio allgyrchol |
| GC | Castio parhaus |
| Meddyg Teulu | Castio marw pwysau |
Amodau materol
| R | Cyflwr materol a ddynodwyd gan y gwerth lleiaf o gryfder tynnol gofyniad ar gyfer y cynnyrch gyda chryfder tynnol gorfodol a gofynion elongation |
| H | Cyflwr materol a ddynodwyd gan y gwerth lleiaf o ofyniad caledwch ar gyfer y cynnyrch gyda gofynion caledwch gorfodol |
Priodweddau mecanyddol
| REh | Cryfder cnwd lleiaf / Mindestwert der oberen Streckgrenze / Limite d elastigit minimale |
| Rm | Cryfder tynnol / Zugfestigkeit / Resistance a la traction |
| A | Lleiafswm elongation / Mindestwert der Bruchdehnung / Allongement minimal |
| J | Prawf effaith rhicyn / Kerbschlagbiegeversuch / Essai de flexion par choc |
|
CuNi1P ( CW108C ) Aloi copr ag aloi isel |