CuNi12Zn29 ( CW405J )
| Gradd : | CuNi12Zn29 |
| Rhif: | CW405J |
| Dosbarthiad: | Aloi cwpanaid |
| Dwysedd | 8.6 g/cm ³ |
| Safon: | EN 1654: 1998 Copr ac aloion copr. Stribed ar gyfer ffynhonnau a chysylltwyr |
| Graddau cyfwerth: | Dim gwybodaeth |
Cyfansoddiad cemegol % o radd CuNi12Zn29 ( CW405J )
| Fe | Mn | Ni | Cu | Pb | Sn | Eraill | - |
| uchafswm 0.3 | uchafswm 0.5 | 11 - 13.5 | 57 - 60 | uchafswm 0.03 | uchafswm 0.03 | cyfanswm 0.2 | Zn — gweddill |
Priodweddau mecanyddol gradd CuNi12Zn29 ( CW405J )
| Rm- Cryfder tynnol (MPa) (R520) | 520-610 |
| Rm- Cryfder tynnol (MPa) (R600) | 600-690 |
| Rp0.20.2% cryfder prawf (MPa) (R520) | 430 |
| Rp0.20.2% cryfder prawf (MPa) (R600) | 550 |
| A— Min. elongation Lo=50mm (%) (R520) | 3-4 |
| A— Min. elongation Lo=50mm (%) (R600) | 2 |
| caledwch Vickers (HV): (H170) (R520) | 170 - 200 |
| Caledwch Vickers (HV): (H190) (R600) | 190 - 220 |
Priodweddau CuNi12Zn29
| Modwlws elastigedd=125 kN/mm ² Dargludedd trydanol=4 MS/m; |
Proses castio
| GS | Castio tywod |
| GM | Castio llwydni parhaol |
| GZ | Castio allgyrchol |
| GC | Castio parhaus |
| Meddyg Teulu | Castio marw pwysau |
Amodau materol
| R | Cyflwr materol a ddynodwyd gan y gwerth lleiaf o gryfder tynnol gofyniad ar gyfer y cynnyrch gyda chryfder tynnol gorfodol a gofynion elongation |
| H | Cyflwr materol a ddynodwyd gan y gwerth lleiaf o ofyniad caledwch ar gyfer y cynnyrch gyda gofynion caledwch gorfodol |
Priodweddau mecanyddol
| ReH | Cryfder cnwd lleiaf / Mindestwert der oberen Streckgrenze / Limite d elastigit minimale |
| Rm | Cryfder tynnol / Zugfestigkeit / Resistance a la traction |
| A | Lleiafswm elongation / Mindestwert der Bruchdehnung / Allongement minimal |
| J | Prawf effaith rhicyn / Kerbschlagbiegeversuch / Essai de flexion par choc |
|
CuNi12Zn29 ( CW405J ) Aloi cwpanaid |