| Gradd : | CuAl9Ni3Fe2 |
| Rhif: | CW304G |
| Dosbarthiad: | Aloi cwpanaid |
| Dwysedd | 7.4 g% 2fcm % C2% B3 |
| Safon: | EN 1653: 1998 Copr ac aloion copr. Plât, dalen a chylchoedd ar gyfer boeleri, llestri gwasgedd ac unedau storio dŵr poeth EN 12165: 1998 Copr ac aloion copr. Stoc gofannu gyr ac anwr EN 12420: 1999 Copr ac aloion copr. Forgings |
| Graddau cyfwerth: | Dim gwybodaeth |
Cyfansoddiad cemegol % o radd CuAl9Ni3Fe2 ( CW304G )
| Fe | Os | Mn | Ni | Al | Pb | Zn | Sn | Eraill | - |
| 1 - 3 | uchafswm 0.1 | uchafswm 2.5 | 2 - 4 | 8 - 9.5 | uchafswm 0.05 | uchafswm 0.2 | uchafswm 0.1 | cyfanswm 0.3 | Cu - gweddill |
Priodweddau mecanyddol gradd CuAl9Ni3Fe2 ( CW304G )
| Rm- Cryfder tynnol (MPa) (R490) | 490 |
| Rp0.20.2% cryfder prawf (MPa) (R490) | 180 |
| A— Min. hiriad wrth dorri asgwrn (%) (R490) | 20 |
| caledwch Vickers (HV): (R490) | 125 |
Proses castio
| GS | Castio tywod |
| GM | Castio llwydni parhaol |
| GZ | Castio allgyrchol |
| GC | Castio parhaus |
| Meddyg Teulu | Castio marw pwysau |
Amodau materol
| R | Cyflwr materol a ddynodwyd gan y gwerth lleiaf o gryfder tynnol gofyniad ar gyfer y cynnyrch gyda chryfder tynnol gorfodol a gofynion elongation |
| H | Cyflwr materol a ddynodwyd gan y gwerth lleiaf o ofyniad caledwch ar gyfer y cynnyrch gyda gofynion caledwch gorfodol |
Priodweddau mecanyddol
| ReH | Cryfder cnwd lleiaf / Mindestwert der oberen Streckgrenze / Limite d elastigit minimale |
| Rm | Cryfder tynnol / Zugfestigkeit / Resistance a la traction |
| A | Lleiafswm elongation / Mindestwert der Bruchdehnung / Allongement minimal |
| J | Prawf effaith rhicyn / Kerbschlagbiegeversuch / Essai de flexion par choc |
|
CuAl9Ni3Fe2 ( CW304G ) Aloi cwpan |