CuAl9-B ( CB330G )
| Gradd : | CuAl9-B |
| Rhif: | CB330G |
| Dosbarthiad: | Aloi cwpan-alwminiwm |
| Safon: | EN 1982: 2008 Copr ac aloion copr. Ingotau a castiau |
| Graddau cyfwerth: | Dim gwybodaeth |
Cyfansoddiad cemegol % o radd CuAl9-B ( CB330G )
| Ychwanegir ôl-ddodiad -B at y dynodiad i adnabod defnydd ar ffurf ingotau |
| Fe | Si | Mn | Ni | Al | Cu | Pb | Zn | Sn | - |
| uchafswm 1 | uchafswm 0.15 | uchafswm 0.5 | uchafswm 1 | 8.2 - 10.5 | 88 - 91.5 | uchafswm 0.25 | uchafswm 0.4 | uchafswm 0.25 | Cu yn cynnwys Ni |
Priodweddau mecanyddol gradd CuAl{ {0}}B ( CB330G )
| Rm- Cryfder tynnol (MPa) (GM) | 500 |
| Rm- Cryfder tynnol (MPa) (GZ) | 450 |
| Rp0.20.2% cryfder prawf (MPa) (GM) | 180 |
| Rp0.20.2% cryfder prawf (MPa) (GZ) | 160 |
| A— Min. hiriad wrth dorri asgwrn (%) (GS) | 20 |
| A— Min. hiriad wrth dorri asgwrn (%) (GZ) | 15 |
| Caledwch Brinell (HBW): (GM) neu (GZ) | 100 |
Proses castio
| GS | Castio tywod |
| GM | Castio llwydni parhaol |
| GZ | Castio allgyrchol |
| GC | Castio parhaus |
| Meddyg Teulu | Castio marw pwysau |
Amodau materol
| R | Cyflwr materol a ddynodwyd gan y gwerth lleiaf o gryfder tynnol gofyniad ar gyfer y cynnyrch gyda chryfder tynnol gorfodol a gofynion elongation |
| H | Cyflwr materol a ddynodwyd gan y gwerth lleiaf o ofyniad caledwch ar gyfer y cynnyrch gyda gofynion caledwch gorfodol |
Priodweddau mecanyddol
| ReH | Cryfder cnwd lleiaf / Mindestwert der oberen Streckgrenze / Limite d elastigit minimale |
| Rm | Cryfder tynnol / Zugfestigkeit / Resistance a la traction |
| A | Lleiafswm elongation / Mindestwert der Bruchdehnung / Allongement minimal |
| J | Prawf effaith rhicyn / Kerbschlagbiegeversuch / Essai de flexion par choc |
|
CuAl9-B ( CB330G ) Aloi cwpan-alwminiwm |