| Gradd : | Cu-FRTP |
| Rhif: | CW006A |
| Dosbarthiad: | Aloi cwpan-tun |
| Dwysedd | 8.9 g% 2fcm % C2% B3 |
| Safon: | EN 1652: 1998 Copr ac aloion copr. Plât, dalen, stribed a chylchoedd at ddibenion cyffredinol EN 1976: 1998 Copr ac aloion copr. Castiwch gynhyrchion copr heb ei drin EN 12163: 1998 Copr ac aloion copr. Gwialen at ddibenion cyffredinol |
| Graddau cyfwerth: | Dim gwybodaeth |
Cyfansoddiad cemegol % o radd Cu-FRTP (CW006A )
| Cu gan gynnwys Ag < 0.015%; |
| Cu | O | Eraill |
| min 99.9 | uchafswm 0.1 | cyfanswm 0.05 |
Priodweddau mecanyddol gradd Cu-FRTP ( CW006A )
| Rm- Cryfder tynnol (MPa) (R240) | 240-300 |
| Rm- Cryfder tynnol (MPa) (R290) | 290-360 |
| Rp0.20.2% cryfder prawf (MPa) (R240) | 180 |
| Rp0.20.2% cryfder prawf (MPa) (R290) | 250 |
| A— Min. hiriad wrth dorri asgwrn (%) (R240) | 15 |
| A— Min. hiriad wrth dorri asgwrn (%) (R290) | 6 |
| A— Min. elongation Lo=50mm (%) (R240) | 8 |
| A— Min. elongation Lo=50mm (%) (R290) | 4 |
| caledwch Vickers (HV): (H065) | 65 - 95 |
| caledwch Vickers (HV): (H090) | 90 - 110 |
Proses castio
| GS | Castio tywod |
| GM | Castio llwydni parhaol |
| GZ | Castio allgyrchol |
| GC | Castio parhaus |
| Meddyg Teulu | Castio marw pwysau |
Amodau materol
| R | Cyflwr materol a ddynodwyd gan y gwerth lleiaf o gryfder tynnol gofyniad ar gyfer y cynnyrch gyda chryfder tynnol gorfodol a gofynion elongation |
| H | Cyflwr materol a ddynodwyd gan y gwerth lleiaf o ofyniad caledwch ar gyfer y cynnyrch gyda gofynion caledwch gorfodol |
Priodweddau mecanyddol
| REh | Cryfder cnwd lleiaf / Mindestwert der oberen Streckgrenze / Limite d elastigit minimale |
| Rm | Cryfder tynnol / Zugfestigkeit / Resistance a la traction |
| A | Lleiafswm elongation / Mindestwert der Bruchdehnung / Allongement minimal |
| J | Prawf effaith rhicyn / Kerbschlagbiegeversuch / Essai de flexion par choc |
|
Cu-FRTP ( CW006A ) Aloi cwpan-tun |